α-Dy2S3 possesses orthorhombic crystal structure having two crystallograpically inequivalent Dy sites. Magnetization process of α-Dy2S3 single crystal after cooling in the high magnetic field of 18 T has been investigated. The magnetization under the field of 18 T along the α-axis on the cooling process from 150 K shows step-like rises at 70 and 40 K and reaches about 9 μB per one Dy3+ at 1.5 K. This value, which corresponds to 90 % of full saturation moment of Dy3+, is much larger than 6 μB obtained at the same conditions after cooling in no magnetic field (zero-field cooling; ZFC). After cooling to 1.5 K, the magnetization while decreasing field shows abrupt drops at 3.0 and 1.7 T, and then comes to 0 μB at 0 T. Subsequently, while increasing field, the magnetization demonstrates a similar curve to that obtained after ZFC without step-like rise below 13.1 T. At μ0H = 13.1 T, the magnetization rises suddenly and agrees with the curve for the decreasing process. This irreversible magnetization process yields extremely broad hysteresis having width of μ0ΔH = 11.4 T. Broader hysteresis and narrower one are also observed at 4.2 and 10 K, respectively.
Content from this work may be used under a CC BY-NC-SA licence (http://creativecommons.org/licenses/by-nc-sa/3.0/). Any further distribution of this work must maintain attribution to the author(s) and the title of the work, journal citation and DOI. Published under licence by IOP Publishing Ltd
Extremely broad hysteresis in the magnetization process of α-Dy2S3 single crystal induced by high field cooling
JPCS_400_3_032010.
(1.07MB)