@article{oai:muroran-it.repo.nii.ac.jp:00008169,
 author = {桃野,  正 and MOMONO, Tadashi and 出川, 恒之 and DEGAWA, Nobuyuki and 片山,  博 and KATAYAMA, Hiroshi and 柴田, 功 and SHIBATA, Isao and 湊, 嘉洋 and MINATO, Yoshihiro and 金山, 達也 and KANAYAMA, Tatsuya and 山口, 和浩 and YAMAGUCHI, Kazuhiro and 酒井, 昌宏 and SAKAI, Masahiro and 牧野, 功 and MAKINO, Isao and 鴨田, 秀一 and KAMOTA, Shuichi and 宮腰, 康樹 and MIYAKOSHI, Yasuki},
 journal = {室蘭工業大学研究報告. 理工編, Memoirs of the Muroran Institute of Technology. Science and engineering},
 month = {Nov},
 note = {application/pdf, Diffusion bonding of WC – 10% Co hard metal to mild steel (S2OC) was carried out by holding at 1000　～　1075℃ for 30 min under the applied pressure of 0.5 ～　1.5 kgf/mm² in vacuum using Ni foil (10 ～ 500　μm in thickness) as an insert-metal. The tensile strength of joints increased through a maximum at 100 μm thickness of Ni foil. Beyond100 μm however, the strength of the joint was almost independent of the thickness of Ni foil. The improvement of the bonding strength was interpreted by the decrease of the thermal stress which is due to the difference in the coefficients of thermal expansion of the hard metal and the steel during the cooling of the joints. Thermal stresses have been estimated by the theory of thermal elastic analysis based on the finite element method.},
 pages = {71--85},
 title = {Ni箔をインサート材としたWC-Co系超硬合金と鉄鋼の拡散接合},
 volume = {41},
 year = {1991},
 yomi = {モモノ, タダシ and デガワ, ノブユキ and カタヤマ, ヒロシ and シバタ, イサオ and ミナト, ヨシヒロ and カナヤマ, タツヤ and ヤマグチ, カズヒロ and サカイ, マサヒロ and マキノ, イサオ and カモタ, シュウイチ and ミヤコシ, ヤスキ}
}