| タイトル |
|
|
タイトル |
β"-アルミナ固体電解質を隔膜に用いたNa/S(Ⅳ)溶融塩電池の特性 |
|
言語 |
ja |
| タイトル |
|
|
タイトル |
A Fundamental Characteristic of the Rechargeable Na/S(Ⅳ) Molten Salt Cell using β"-Almina Solid Electrolyte |
|
言語 |
en |
| 言語 |
|
|
言語 |
jpn |
| 資源タイプ |
|
|
資源タイプ識別子 |
http://purl.org/coar/resource_type/c_6501 |
|
資源タイプ |
departmental bulletin paper |
| アクセス権 |
|
|
アクセス権 |
open access |
|
アクセス権URI |
http://purl.org/coar/access_right/c_abf2 |
| 著者 |
嶋影, 和宜
咲間, 光廣
戸田, 茂雄
佐藤, 忠夫
|
| 抄録 |
|
|
内容記述タイプ |
Abstract |
|
内容記述 |
Recently, the development of new rechargeable cell has been interested in the load leveling of an electric power and the use as an electric automobile power. In the current investigation, the fundamental characteristic of a rechargeable sodium/ sulfur (IV) molten salt cell, which was previously developed by G. Mamantov in U.S.A., has been examined from the analysis of the charge-discharge curve. A laboratory cell was made of pyrex glass containing β” –alumina solid electrotype. The experimental results obtained were summarized as follows: The laboratory cell constructed could be continuously moved for 3 months at the temperature of 473 K. Two plateaus giving stable electromotive forces were observed at the discharge process. Electromotive forces for the corresponding plateaus were thermodynamically based on chemical reactions of cell. The average voltage was high above 3.5V for the first plateau region. The characteristic of cell such as energy efficiency, energy density and utilization of sulfur was to depend on current density at the discharge process. The performance of cell was also considered to be affected by the ionic conductivity of solid electrotype. The cycle number of the charge-discharge was above 175 and the final discharge capacity was about 21.2 Ah. |
|
言語 |
en |
| 書誌情報 |
ja : 室蘭工業大学研究報告. 理工編
en : Memoirs of the Muroran Institute of Technology. Science and engineering
巻 39,
p. 1-16,
発行日 1989-11-10
|
| 出版者 |
|
|
出版者 |
室蘭工業大学 |
|
言語 |
ja |
| 論文ID（NAID） |
|
|
関連タイプ |
isIdenticalTo |
|
|
識別子タイプ |
NAID |
|
|
関連識別子 |
40003627696 |
| 日本十進分類法 |
|
|
主題Scheme |
NDC |
|
主題 |
572.1 |
| ISSN |
|
|
収録物識別子タイプ |
PISSN |
|
収録物識別子 |
05802415 |
| 書誌レコードID |
|
|
収録物識別子タイプ |
NCID |
|
収録物識別子 |
AN00238225 |
| 権利 |
|
|
言語 |
ja |
|
権利情報 |
copyright© 1989 室蘭工業大学 |
| 著者版フラグ |
|
|
出版タイプ |
VoR |
|
出版タイプResource |
http://purl.org/coar/version/c_970fb48d4fbd8a85 |
| フォーマット |
|
|
内容記述タイプ |
Other |
|
内容記述 |
application/pdf |
kiyo39_rikou_pp1-16.pdf (1.2 MB)